news

Features:
1. Green environmental protection, odorless, catalyst-free, fast curing, wearing general basic protection during construction, can be applied on any curved surface, inclined surface and vertical surface
2. It is not sensitive to moisture and humidity, and is not affected by the dryness and humidity of the environment during construction. It can be constructed on both wet and dry surfaces, and it is easy to operate.
3. It has strong environmental adaptability, and the construction meets the thickness requirements, which overcomes the disadvantages of poor bonding and lax stubble connection in the previous split-layer construction.
4. It has good adhesion to the surface of reinforced concrete, anti-swelling strength, toughness, oil resistance and water erosion resistance.
5. It has excellent freeze-thaw resistance and thermal stability.
6. It has good air-tightness and water impermeability. It is impermeable to water for 24 hours under 3Mpa pressure, and the material has no change.
7. Various pigments and fillers can be added, and products of different colors can be made according to customer requirements to meet the market.
8. Under the condition of long-term immersion in water, the anti-corrosion and waterproofing of buildings on the upstream and downstream surfaces will not fall off and will not blister.
9. This product has high anti-aging, anti-ultraviolet, strong resistance to dry and wet alternation, good anti-microbial and corrosion performance of acid, nitric, alkali, salt, gasoline, coal and diesel.
10. It will not be strong after cold replacement, excellent weather resistance, no powdering, no tortoise, good thermal stability, high material compaction strength, no joints in scraping and coating, and outstanding anti-corrosion and waterproof performance.

Product technical indicators:
(1) Adhesion of polyacrylate emulsion anti-corrosion waterproof mortar
1. Bonding with steel plate: The bonding strength of polyacrylate emulsion anti-corrosion waterproof mortar and steel plate is more than 2 times higher than that of ordinary mortar, and the bonding strength will be improved more under dry curing.
2 Compared with the bond strength of the old mortar and the ordinary cement mortar, the bond strength of the wet surface of the polyacrylate emulsion anti-corrosion and waterproof mortar can be increased by 3 to 4 times.
(2) Crack resistance of polyacrylate emulsion anti-corrosion and waterproof mortar: the elongation of polyacrylate emulsion and liquid anti-corrosion and waterproof mortar is more than 1 times higher than that of ordinary mortar maintained under the same conditions. In the case of dry curing, it is 2~3 times higher than ordinary mortar, and its elongation rate can reach 900×10-6. Polyacrylate emulsion anti-corrosion waterproof mortar
The tensile strength can generally be increased by 40%~60%, and its elastic modulus is about 50%~63% of ordinary mortar.
However, the early shrinkage deformation of polyacrylate emulsion anti-corrosion waterproof mortar is only 6% of that of ordinary mortar.

Scope of application:
1. The building structure is reinforced with concrete, and the civil air defense facilities are waterproof and leak-proof.
2. Anti-seepage treatment of reservoir dams and ports.
3. Anti-chemical corrosion buildings such as hot water pools, landfills, chemical warehouses, chemical tanks, etc.
4. Concrete repair of pavement, bridge deck, tunnel and culvert.
5. Anti-leakage treatment for roofs, toilets and basements of industrial and civil buildings.
6. Steel structure and reinforced concrete waterproof.
7. Anticorrosion in sewage treatment plant.
8. Environmentally sound anticorrosion such as bioengineering, pharmaceuticals, tap water plants, etc.
9. Protection of water pipelines, etc.